Shenzhen Hong Ye Jie Technology Co., Ltd.  

Product Name: Electronic Potting Compound Silicone Rubber Model NO.: HY-9055 silicon Form: Liquid Rubber Appearance: Liquid Material: Silicone Rubber Raw Material: Natural Rubber Color: Translucent Feature: Liquid Sample: Available Purity: 100% Certifications: RoHS, MSDS, SGS, ISO9001:2000 Minimum Order Quantity: 200 Kilogram Brand Name: Hong Ye Silicone Rubber Place of Origin: Guangdong China Application: Silicone Rubber for Electronic Potting Trademark: Hong Ye silicone rubber Transport Package: 20kg/Drum, 200kg/Drum Specification: RoHS, MSDS, SGS, ISO9001: 2000 Origin: Shenzhen, China HS Code: 39100000 Product Description general electric potting silicone rubber material general electric potting silicone rubber Product FeatureHY 9055 is akind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate),PP,ABS,PVC, etc. and metal materials.general electric potting silicone rubber Typical ApplicationHY 9055 could be applied to- high powered electronics,- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.-It can be broadly used for LED screen, Wind Power Generator,PCB substrate, etc.general electric potting silicone rubber TECHNICAL GUIDELINES1, Pls put part Aand part Bin separate container and stir evenly before mixing the two part together.2, Mixing Ratio: part A: part B= 1:13, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is alittle thick,then the curing time will be alittle longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100°C, the silicone will cure in 15 minutes; while in 25°C room temperature, the silicone will cure around 8hours.general electric potting silicone rubber Notes:1.The following material may hinder the curing of HY 9055, So pls use after the test. When necessary, pls clean the application areas.Organotin compound or Condensation silicone with organotin;Sulphur, sulfide and sulfur rubber materials;Amine compounds as well as contains the amine materials;Pewters solder flux;2. HY 9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.3. HY 9055 belongs to non-dangerous goods, but keep away from mouth and eyes.4. When it gets stratified after aperiod of storage, Please mix it evenly before using,which does not affect the performance.Standard DatasheetModelHY-215TypeGel-typeComponentsABAppearance (liquid)black /transparent /whiteyellowMixing ratio (%)101Viscosity (Pa.s)2~40.005Pot life(25°C) (mins)20 -30Curing time (mins)2 -4Hardness shore A15 ±2Tensile strength (Mpa)0.5 -1.5Elongation at break (%)30 -50Dielectric strength (kv/m-1)20Specific inductive capacity(1MHz)2.8 -3.2Breakdown voltage (KV.mm-1)16Volume resistivity (Ω)1×1014Dielectric loss factor (1MHz)1×10-3PackageMore information ,pls feel free to contact Michael:Mob:+8618938867553Tele.: 075589212386